Overview
Continuous development in Electric Arc Furnaces & Ladle Technology has led to the need of Graphite Electrodes of very stringent quality. Emergence of DRI, HBI, Sponge Iron as potential source of raw material as against steel scrap revolutionized Electric Steel Making Industry, Higher Capacities of Electric Arc Furnace with bigger size, UHP Electrodes are common requirements of Electric Steel Industry. The emphasis is on better consumption norms & least electro mechanical problems.CEL keeps abreast of technological developments in EAF's at its customers end in order to carry on R&D efforts to meet their ever-changing and or their demanding requirements.

For your requirements, please contact us.

Regular Power (RP) Grade Graphite Electrodes

Typical Physical Properties (GRADE:CH):
BULK DENSITY g/cm3	>1.65
SPECIFIC RESISTANCE µm	>7.0
FLEXURAL STRENGTH Mpa (min)	>10
YOUNG'S MODULUS Gpa (max)	>14
ASH CONTENT (max) %	>0.2
CTE x10-6/Deg.C	>1.9

High Power (HP) Grade Graphite Electrodes

TYPICAL PHYSICAL PROPERTIES(GRADE:CPH)
BULK DENSITY g/cm3	>1.68
SPECIFIC RESISTANCE µm	>6.5
FLEXURAL STRENGTH Mpa (min)	>11
YOUNG'S MODULUS Gpa (max)	>16
ASH CONTENT (max) %	>0.2
CTE x10-6/Deg .C	>1.9

Ultra High Power (UHP) Grade Graphite Electrodes

TYPICAL PHYSICAL PROPERTIES (GRADE:UHP)
BULK DENSITY g/cm3	>1.71
SPECIFIC RESISTANCE µm	>6.0
FLEXURAL STRENGTH Mpa (min)	>11
YOUNG'S MODULUS Gpa (max)	>16
ASH CONTENT (max) %	>0.2
CTE x10-6/Deg.C	>1.5